2K-Derocryl Lack 70 ST

Two component topcoat on acrylic resin basis, chemical cured with poly-isocyanate (polyurethane).

General information
2K-Derocryl Lack 70 ST

Field of application

  • Corrosion protection for Iron and Steel.
  • Certificate (180159 ILF) as monolayer with 120 µm dft. System with 2K-DP Protec certified C4 high (180160 ILF),
  • with 2K-DPGrund HD certified C5 high (180162 ILF).
  • Good flow during processing in the low-pressure spraying with hardener HL 106 (MVH = 5: 1)

Product properties

  • High Solid
  • Resistance to light acids
  • Resistance to weak bases
  • Coating systems for low temperatures
  • Good UV-stability
  • Fast curing

Technical Specification
2K-Derocryl Lack 70 ST

Colours RAL 5010, RAL-colour chart with exceptions, apart from RAL 9006/9007.
Flash point >23 °C
Temperature stability -20 up to 120 (short-term up to 150) °C
Gloss Satin glossy, appr. 40 U in 60° angle
Potential dry film thickness in one working process 60 up to 120 µm
Mixing ratio Hardener HL 115 Hardener HL 401
(Basis:hardener) by weight 8:1 10:1
(Basis:hardener) by volume 5,3:1 7:1
Pot life in hours 2,5 2
Viscosity Appr. 30 sec running time (DIN 6 mm pot) Thixotrope
Density in kg/l 1,37 1,39
Solid content in % 71 72
Solid volume in % 54 56
Theoretical spreading capacity
  • 6,75 m²/l at 80 µm DFT
  • 4,93 m²/kg at 80 µm DFT
  • 7 m²/l at 80 µm DFT
  • 5,04 m²/kg at 80 µm DFT
Recommended film thickness 150 µm WFT corresponds to 80 µm DFT 150 µm WFT corresponds to 80 µm DFT
Drying (DIN EN ISO 1517) 80 µm DFT 80 µm DFT
Dust-dry (Tg1) After 40 min After 30 min
Touch-dry (Tg4) After 5 h After 4 h
Dry (Tg6) After 6 h After 6 h
Cured chemically After 7 days After 7 days
Accelerated drying 30 min. at 60°C possible, after 10 min. flash-off time
Interval for overcoating
  • after 6 h with itself
  • after 8 h with itself

Note

  • The specifications are related to the prepared mixture and are based on standard atmospheric conditions 23/50, DIN 50014.
  • Lower temperatures and/or higher humidity will prolong drying and hardening.
  • It is possible to use this material to limit frost temperature (possibly solvents are necessary).

Safety information
2K-Derocryl Lack 70 ST

(See Security Data Sheet)

VOC-level Appr. 389 g/l
Solvent content Appr. 29 % by weight Appr. 27 % by weight
Aromatic content Appr. 11 % by weight

Storage
2K-Derocryl Lack 70 ST

Storage

  • In dry, cool rooms, if possible frost-proof
  • Ensure good ventilation

Shelf life

  • 6 month from date of delivery when in unopened original containers in cool and dry conditions

Application methods
2K-Derocryl Lack 70 ST

Mixing ratio

  • Stirr homogeneous, preferably with mechanical stirrer
  • Mix base paint and hardener according to the mixing ratio as specified

Airless spraying

  • Flow pressure 180 - 210 bar
  • Nozzle size 0,013 - 0,015 inch (0,33 - 0,38 mm)
  • Spraying angle according to the geometry and size of the object to be laquered

Compressed air spraying

  • Can be applied as delivered
  • Spraying pressure 2 - 5 bar
  • Nozzle size 1,3 - 1,6 mm
  • Adjust to spraying viscosity (appr. 60 s DIN 4 mm) adding appr. 3 % Derocryl-Verdünnung (two component products: after mixing)

Electrostatic application

  • Can be applied as delivered

Dipping

  • Can not be applied as delivered

Other methods

  • Roller and brush application for repair work is possible

Thinner

  • Max. 5% Derocryl-Verdünnung

Cleaning

  • Rinse immediately with Derocryl-Verdünnung

Preparation of support

  • Shot blasting to a purity according to SA 2½
  • If necessary clean with high pressure-cleaner and turbo-cleaner-solution
  • Mill scale, welding residues, dust and dirt on the surface which might reduce adhesion have to be carefully and thoroughly removed
  • Clean primer of the coating system

General remarks

  • During coating and drying the humidity should be min. 30 % / max. 85 %
  • During coating and drying the environmental temperature should be min. 5°C / max. 30°C
  • Object temperature at least 3° C above dew point.

Example for a system

  • Primer coat: 2K-Deripox Protec ZP
  • Finish coat: 2K-Derocryl Lack 70 ST

Derisol Hydro Shopprimer

Newest Shopprimer Generation

Shopprimer Hydro EcoWeld

2K-Hydropox Shopprimer

See the products

2K-Derocryl Lack AgriFlex

ACE- Agriculture Construction Earthmoving Equipment

High Gloss DTM High Solid. Excellent corrosion protection at 60 µm DFT.

Product Information

2K-Derocryl Lack DTM Rapid

HS One layer coat with extremly fast drying at high layer thicknesses

Two component coat on acryl resin. Economic coating system for steel

See more details

The general information and descriptions contained in this specification are provided to the best of our knowledge. Our information and specifications do not constitute warranted characteristics in the legal sense. Any advice for preparation and application which may be provided verbally, in writing or by means of experiments is of general nature only, and any property rights of third parties are also to be regarded in this context. Our general instructions do not release you from your obligation to check the suitability of the products supplied by our company for the intended methods and purposes of application. Particular in those cases when our supplied material will be applied with products from other sources. The products are prepared, applied and used outside of our sphere of control and thus fall solely within the user´s scope of responsibility.
Our general terms of sale and delivery apply as agreed.

Quick access to product information.

Dr. Demuth Derisol Lackfarben GmbH & Co. KG

Hillerser Straße 8, 37154 Northeim
Telefon +49 5551 / 97940
Telefax +49 5551 / 979430

Cookies facilitate the provision of our services. By using our services, you agree that we use cookies. For more information on privacy, please visit the following link Data protection statement