2K-Deripox Grund 60 HS

Two component primer with anti-corrosive pigments (zinc-phosphate) on epoxy resin basis, chemical cured with polyamine adduct

General information
2K-Deripox Grund 60 HS

Field of application

  • Protection against corrosion for iron and steel and zinced supports
  • Primer for low film thickness

Product properties

  • High Solid
  • Silicon-free
  • Contains zincphosphate
  • Resistance to chemicals (on request)
  • Resistance to mineral oils
  • High surface hardness
  • Fast drying
  • Recoatability: with two component topcoats
  • Release by the company Hensel GmbH, Germany as a primer for fíre protection systems F30- F90

Technical Specification
2K-Deripox Grund 60 HS

Colours redbrown, light-grey.
Flash point >23 °C
Temperature stability -20 up to 160 °C
Gloss Mat
Potential dry film thickness in one working process 50 up to 100 µm
Mixing ratio Hardener HL 500
(Basis:hardener) by weight 10:1
(Basis:hardener) by volume 5,7:1
Pot life in hours 8
Viscosity Appr. 17 sec running time (DIN 6 mm pot)
Density in kg/l 1,56
Solid content in % 75
Solid volume in % 56
Theoretical spreading capacity
  • 11,2 m²/l at 50 µm DFT
  • 7,18 m²/kg at 50 µm DFT
Recommended film thickness 100 µm WFT corresponds to 60 µm DFT
Drying (DIN EN ISO 1517) 50 µm DFT
Dust-dry (Tg1) After 25 min
Touch-dry (Tg4) After 2 h
Dry (Tg6) After 6 h
Cured chemically After 7 days
Interval for overcoating
  • after 5 h with two component Deripox topcoats
  • Max. after 6 months without slightly sanding
  • after 6 h with two component Derocryl topcoats

Note

  • The specifications are related to the prepared mixture and are based on standard atmospheric conditions 23/50, DIN 50014.
  • Lower temperatures and/or higher humidity will prolong drying and hardening.
  • Application below +5 °C is not possible.

Safety information
2K-Deripox Grund 60 HS

(See Security Data Sheet)

VOC-level Appr. 380 g/l
Solvent content Appr. 25 % by weight
Aromatic content Appr. 19 % by weight

Storage
2K-Deripox Grund 60 HS

Storage

  • In dry, cool rooms, if possible frost-proof
  • Ensure good ventilation

Shelf life

  • 6 month from date of delivery when in unopened original containers in cool and dry conditions

Application methods
2K-Deripox Grund 60 HS

Mixing ratio

  • Stirr homogeneous, preferably with mechanical stirrer
  • Mix base paint and hardener according to the mixing ratio as specified

Airless spraying

  • Flow pressure 160 bar
  • Nozzle size 0,011 inch (0,28 mm)
  • Spraying angle according to the geometry and size of the object to be laquered

Compressed air spraying

  • Spraying pressure 4 - 6 bar
  • Nozzle size 1,5 - 2 mm
  • Adjust to spraying viscosity (appr. 30 s DIN 4 mm) adding appr. 8 % Deripox-Verdünnung (two component products: after mixing)

Electrostatic application

  • Can be applied as delivered
  • Conductance of the material: 1000 kΩ

Dipping

  • Can not be applied as delivered

Other methods

  • Roller and brush application is possible in the quality as delivered
  • Double application is possible in viscosity as delivered

Thinner

  • Max. 10% Deripox-Verdünnung

Cleaning

  • Rinse immediately with Deripox-Verdünnung

Preparation of support

  • Shot blasting to a purity according to SA 2½
  • If necessary clean with high pressure-cleaner and turbo-cleaner-solution
  • Sweeping for zinced supports
  • Mill scale, welding residues, dust, soluble residues from chemical pretreatments and zinc reaction products which might reduce adhesion have to be carefully and thoroughly removed

General remarks

  • During coating and drying the humidity should be min. 10 % / max. 85 %
  • During coating and drying the environmental temperature should be min. 5°C / max. 30°C
  • Object temperature at least 3° C above dew point.

Example for a system

  • Primer coat: 2K-Deripox Grund 60 HS
  • Finish coat: 2K-Derocryl Lack MS

Derisol Hydro Shopprimer

Newest Shopprimer Generation

Shopprimer Hydro EcoWeld

2K-Hydropox Shopprimer

See the products

2K-Derocryl Lack AgriFlex

ACE- Agriculture Construction Earthmoving Equipment

High Gloss DTM High Solid. Excellent corrosion protection at 60 µm DFT.

Product Information

2K-Derocryl Lack DTM Rapid

HS One layer coat with extremly fast drying at high layer thicknesses

Two component coat on acryl resin. Economic coating system for steel

See more details

The general information and descriptions contained in this specification are provided to the best of our knowledge. Our information and specifications do not constitute warranted characteristics in the legal sense. Any advice for preparation and application which may be provided verbally, in writing or by means of experiments is of general nature only, and any property rights of third parties are also to be regarded in this context. Our general instructions do not release you from your obligation to check the suitability of the products supplied by our company for the intended methods and purposes of application. Particular in those cases when our supplied material will be applied with products from other sources. The products are prepared, applied and used outside of our sphere of control and thus fall solely within the user´s scope of responsibility.
Our general terms of sale and delivery apply as agreed.

Quick access to product information.

Dr. Demuth Derisol Lackfarben GmbH & Co. KG

Hillerser Straße 8, 37154 Northeim
Telefon +49 5551 / 97940
Telefax +49 5551 / 979430

Cookie Settings

We use cookies to improve your experience and to provide you with personalized content. By using this website you agree to our cookie policy

Necessary Cookies
Statistical Cookies
Third-party Cookies
Accept Change Settings
www.dr-demuth.com

Cookie Settings

More information on how we use cookies in our cookie policy.

­

Necessary Cookies

Without these Cookies services you have asked for cannot be provided.

Statistical Cookies

Allow anonymous usage statistics so that we can improve our offering.

Third-party Cookies

Third-party cookies that are integrated to deliver personalized ads for you.

Cookies We use on This Site